FKM, HNBR, PU, EPDM, Iir, Pvmq, FPM, Eco, Csm, Acm, NBR, PVC, Rubber Counpound, Direct Factory Sale, Rubber

• Raw Material: Synthetic Rubber
• Material: Rubber Compound
• Appearance: Colored Customized
• Shipping Cost: Estimated freight per unit.: about shipping cost and estimated delivery time.
• Currency: US$
• Return&refunds: You can apply for a refund up to 30 days after receipt of the products.
• Model NO.: SaneZen Rubber Series
• Form: The Massive Raw Rubber
• Technical Specification: Customized
• Application: Extrusion, Molded Articles
• Characteristics: Translucent, Natural Color
• Natural Color: Translucent
• Fluorine Content: 60±5%
• Volatile Content: <1.0%
• Transport Package: 20kg Percardboard Boxes.
• Specification: 50*35*15
• Trademark: Lixin
• Origin: China
• HS Code: 4002991100
• Production Capacity: 50000
• Package Size: 100.00cm * 100.00cm * 100.00cm
• Package Gross Weight: 25.000kg

Product Description

SaneZen Group is one of the largest and well-known brand rubber raw materials manufacturers in China. Four technical R&D centers owned by SaneZen Group.
     
we are manufacturer of Polymers : ACM ,NBR-PVC Rubber-Plastic Blends,and Silicone Rubber  and ALL kinds of rubber compound of FKM.HNBR.CR.AEM.ACM,EPDM,NBR etc.  detailed product information. you can refer to click on the following hyperlink in the follow image below: or you can reach us by email or phone.
     
-Rubber compound:
FKM premixed rubber, HNBR hydrogenated nitrile rubber compound ,such as FKM, HNBR,PU ,EPDM,IIR , PVMQ, FPM,ECO,CSM,Acm, NBR, PVC,etc. around 33 types of rubber compound. flexiable to be customized  base on your requirments.

-NBR-PVC Rubber-Plastic Blends
mainly covers industries of automobile manufacturing, oil field exploitation, air conditioning, construction industry, electrical industry, aerospace industry, military industry, etc. NV rubber and plastic blend rubber is suitable for manufacturing oil pipes, rubber pipes, wires and cables, sheaths, belts, soles, rollers and other products.
   
-ACM series
can divided into two type: Active chlorine type and Carboxyl type. ACM are suitable for automobile oil seals, O-rings, cylinder gaskets and transformer seals, and are widely used in automobiles, motorcycles, ships, electric power field etc.

-Silicone Rubbers
We have full three types of silicone rubbers of methyl vinyl silicone rubber, phenyl silicone rubber, fluorine silicone rubber,Our silicone rubber products mainly cover industries of automobile, aviation, electronic appliances, construction, electricity, medical and health, household goods, etc.,

Excellent physical properties, excellent technology research and development team, friendly price, stable quality, fast logistics and delivery system, which let us win unanimous praise from peers and customers.


Please click the icon (highperlink) to jump to different products in the same series that you may be interested in.





 

Rubber Classification

 

 

product name			LXF100CA	LXF200CA
project	Test Methods	unit	Typical value
Mooney viscosity(ML 1+4@100ºC)			53	48
Vulcanization performance test:180ºC×5min×1arc
Minimum torque	ASTM D2048	lb-in	0.40	0.38
Maximum torque		lb-in	9.02	8.46
Scorch Time TS2		s	72	73
Positive vulcanization time TC90		s	140	136
1,Mechanical properties 1.1 First vulcanization: 175ºC×10min, Second vulcanization: 230ºC×16h
Proportion	ASTM D297	g/cm3	1.938	1.936
Hardness (Shore A)	ASTM D2240	Points	70	70
Tear strength	ASTM D412	MPa	11.28	10.58
Elongation at break		%	257	248
M100		MPa	5.45	5.40
1, Mechanical properties 1.2 Changes in properties after aging at 200°C for 504 hours
Hardness (Shore A) change	ASTM D2240	Points	+3	+5
Change in breaking strength	ASTM D412	%	-4.2	-8.0
Elongation at break change	ASTM D412	%	-15.5	-22.5
2,Oil resistance 2.1 Changes in resistance to FAM B oil at 23°C for 48 hours
Hardness (Shore A) change	ASTM D2240	Points	-6	-10
Volume change rate change	ASTM D471	%	+10.5	+16.5
2,Oil resistance 2.2 Performance after aging and drying at 100°C for 48 hours after being resistant to FAM B oil at 23°C for 48 hours
Hardness (Shore A)	ASTM D2240	Points	70	70
Tear strength	ASTM D412	%	10.28	9.98
Elongation at break	ASTM D412	%	245	224
volume change rate	ASTM D471	%	+0.23	+0.52
2,Oil resistance 2.3 Diesel resistance change at 23°C for 48 hours
Hardness (Shore A) change	ASTM D2240	Points	0	-3
volume change rate	ASTM D471	%	-0.03	+3.98
2,Oil resistance 2.4 Performance after aging at 23°C for 48 hours against diesel oil and drying at 100°C for 48 hours
Hardness (Shore A)	ASTM D2240	Points	70	69
tear strength	ASTM D412	%	10.25	9.67
Elongation at break	ASTM D412	%	238	228
Volume change rate%	ASTM D471	%	+0.34	+0.92
2,Oil resistance 2.5 Biodiesel resistance (RME) performance at 80°C for 504 hours
Hardness change (Shore A)	ASTM D2240	Points	-2	-4
Volume change	ASTM D471	%	+3.1	+5.2
Tear strength	ASTM D412	MPa	8.94	7.54
Elongation at break		%	269	237
2,Oil resistance 2.6 Resistance to 5W/30 engine oil (RME) at 80°C for 504 hours
Hardness change (Shore A)	ASTM D2240	Points	-1	-4
Volume change	ASTM D471	%	+3.52	+9.62
tear strength	ASTM D412	MPa	9.05	7.24
Elongation at break		%	215	189
3,Compression set at 150°C for 24 hours (the vulcanization condition of the sample 1^st curing at 175°C×10min and 2^nd curing at 230°C×16h)
Compression set	ASTM D395	%	26.48	23.48
4,Ozone resistance 80pphm×20% for elongation×40ºC×120 hours
Cracked or not	ASTM D1171	/	NO	NO
5,Low temperature retraction TR10
TR10	GB 7758	ºC	-20	-25

 

Our factory:

 

 

Our equipment:

 

 

Our certificates:

 

Dlivery & Shipment:

 

FAQ:

 

Q: Are you a factory or trading company?
A: We are  rubber raw material manufacturer and owned 3 factories.

Q: Where is the loading port and How do you ship the goods?
A: Our factory is nearby Shanghai Port, but loading port can be negotiated. We could ship by sea, by air or by express(EMS, UPS, DHL, TNT, FEDEX and etc). Please confirm with us before placing orders.

Q: How can we guarantee the products' quality?
A: All the products must be tested refers to key specifications during the production and final inspection before shipment.
 
Q: What about the lead time?
A: It depends on the order quantity you place the order. Usually sample needs 5-8 working days, mass production needs 15-30 days.